Acid or acid salt wash of a metal chloride layer of an ion selective electrode

ABSTRACT

There are disclosed a process and the product produced by the process, of making an ion selective electrode for chloride. The process features, after forming a metal chloride layer, the step of washing the electrode in an organic acid, inorganic acid, or a solution of a salt of the acids having certain specified properties.

This application is a continuation-in-part application of U.S. Ser. No. 813,162 filed on Dec. 24, 1985, now abandoned.

FIELD OF THE INVENTION

This invention relates to a process, and its product, of forming an ion selective electrode. It more particularly concerns the formation of the chloride electrode.

BACKGROUND OF THE INVENTION

Ion selective electrodes, hereinafter ISE's, have become a significant part of the clinical chemists' arsenal in analyzing for analytes in biological fluids. Such ISE's allow for the activity determination of ionic analytes such as Cl.sup.⊖, Na.sup.⊕, K.sup.⊕ and HCO₃.sup.⊖. These ionic analytes are useful in diagnosing, e.g., various acidosis conditions, and in the case of Cl.sup.⊖, adrenal disease and renal failure.

For the Cl.sup.⊖ ISE, useful electrode constructions and preparations are described in U.S. Pat. Nos. 4,214,968, issued July 29, 1980, and 4,199,411, issued Apr. 22, 1980. Such Cl.sup.⊖ ISE is preferably prepared by forming a layer of silver on a suitable support, and thereafter converting a surface portion of the silver layer to silver chloride by treating the silver layer with a chlorochromate bath or wash. Useful examples of such a bath or wash are described in the aforesaid patents.

The most preferred construction of the Cl.sup.⊖ ISE is one in which a thin overlayer, preferably of a cellulose ester, is formed on the silver chloride layer, as described in the aforesaid '411 patent. Although such an overlayer is not essential, it is useful in those occasional instances in which there is a potential for significant uric acid interference in the biological liquid being analyzed. That is, such overlayer has been found to be effective in reducing such interference (as well as interference from e.g., bromide ions). Uric acid, as is well known, is an endogenous purine that can be found as a natural metabolite in human body liquids.

Although such an overcoated Cl.sup.⊖ ISE has been found to be very effective and useful, there have been a few instances in which the ISE was found to produce a large negative bias, representing a falsely reduced Cl.sup.⊖ concentration, when used with test samples containing purines other than uric acid, e.g., hypoxanthine, allopurinol, caffeine, adenine, xanthine, theophylline and the like. These results are reported in, e.g., Clin. Chem., Vol. 30, p. 1113-1114 (1984). Such purines can occur in the patient sample from, e.g., treatment for cancer such as leukemia, when there is also acute renal failure.

Thus, prior to this invention the problem has been to provide a way of reducing the bias in the Cl.sup.⊖ ISE that can be caused by purines other than uric acid. This has not been a facile problem to resolve, for the following reasons:

One approach was to form the AgCl layer by an alternative method different from the chlorochromate wash noted above. In such cases, the purines, noted above do not create the bias problem. However, this solution is not particularly desirable, because the use of chlorochromate oxidizing agents appears to be more effective than the noted alternatives, in reducing interference from bromide ions.

Another approach that was considered was a decrease in the permeability of the cellulose ester overcoat so as to hinder the other purines, as well as uric acid, from reaching the AgCl surface. However, this is unsatisfactory because such a decreased permeability renders the ISE less able to be operative within the desired read time, e.g., about three minutes.

For the noted reasons, the purine bias problem caused by the purines other than uric acid remained to be solved by the instant invention.

SUMMARY OF THE INVENTION

This invention is based on the discovery that a step of washing the surface of the silver chloride layer in an appropriate acid is effective, by an unknown surface phenomenon, to reduce the negative bias caused by the presence of purines.

More specifically, in accord with one aspect of the invention there is provided a process for making an ion selective electrode selective for chloride, comprising the steps of (a) forming a layer of silver on a support, and (b) oxidizing a surface portion of the silver layer with a bath comprising a chlorochromate, to form silver chloride. This process is improved in that, after step (b) a further step is included of washing the electrode in an organic acid, inorganic acid, or salt of the organic or inorganic acid, provided that

(a) the acid has a pKa<4.0 and a silver solubility product pK_(sp) <10.0, in a concentration and for a length of time effective to reduce negative biases created by purine interferences when using an electrode prepared without the further step; and

(b) the salt:

(i) is soluble in water at ≧0.001M,

(ii) yields an aqueous pH of ≦7.0, and

(iii) comprises ions that do not dissolve the silver chloride, the cations being univalent or divalent cations only.

In accord with another aspect of the invention, there is provided an ion selective electrode selective for chloride, comprising a support, a layer of silver on the support, and a layer of silver chloride on the silver layer. The electrode is improved in that the silver chloride layer has a surface prepared by washing said electrode in an organic or inorganic acid having a pKa and pK_(sp), and at a concentration and for a length of time, noted above, or in a solution of a salt of an organic or inorganic acid, provided that the salt has the features noted above in the previous paragraph.

As used herein, the purine negative biases noted above are deemed to be "reduced" if there is at least a 10% reduction in the negative bias that occurs for an identical electrode prepared without using the invention, and when testing with a purine interference that creates a negative bias in the absence of the invention. Thus, "purine interference" means, from a purine that actually alters the expected reading in the absence of the invention (which is not the case for just uric acid when using an ISE having a cellulose acetate overcoat.)

Thus, it is an advantageous feature of the invention that a Cl.sup.⊖ ISE is provided with a reduced or no negative bias in the presence of purines, compared to what would be the case without using the invention.

It is a related advantageous feature of the invention that such an ISE is provided without sacrificing its ability to avoid biases created by bromide interference.

It is another related, advantageous feature of the invention that such an ISE is provided from which ion activity values can be read after 3 minutes of contact with a biological liquid.

DESCRIPTION OF THE PREFERRED EMBODIMENTS

The present invention is particularly described with reference to a preferred Cl.sup.⊖ ISE prepared with a cellulose ester overcoat on a silver chloride layer formed on a silver conductive metal layer. In addition, it is also useful in reducing negative purine biases for such Cl.sup.⊖ ISE's lacking such overcoats, and regardless of the conductive metal selected. That is, the process can be applied to a layer of MCl, where M is a conductive metal such as Ag, Ni, Cu and Au. If no cellulose ester overcoat is present, then the wash step is effective even against uric acid as the purine.

As used herein, "negative bias" refers to an increased positive ISE potential that represents an increase in Ag.sup.⊕ activity. The net effect is to predict a lower Cl.sup.⊖ concentration than is actually the case.

The conventional steps of preparing the Cl.sup.⊖ ISE are, as noted above, described in the aforesaid two U.S. patents. For the reasons noted, the preferred oxidizing step to form the AgCl employs a chlorochromate bath at a temperature of 23°±2° C. Such a bath can comprise a chlorochromate of any cation, e.g., Na.sup.⊖ or K.sup.⊕. The preferred bath features the K.sup.⊕ form, in a concentration of from about 0.002M to about 0.2M. The most preferred composition of such a bath comprises 0.15M HCl, 0.2M KCl, and 0.034M K₂ Cr₂ O₇. In the most preferred use of this bath, the silver layer passes through the bath at 3-9 m/minute to convert about 25-40 weight % of the silver to silver chloride, at the surface.

An optional, but preferred, final step is the overcoating of the silver halide layer with the layer (cellulose ester, e.g., cellulose acetate, noted above). Such an overcoat and its preparation are amply described in the aforesaid '411 patent. It is because of such overlayer that the reduction in negative bias achieved by the invention is apparent for purines other than uric acid. That is, the overcoat itself is significantly effective in preventing a bias due to uric acid. Of course, if the overcoat is omitted, then the invention will demonstrate a reduction in negative bias, compared to an untreated ISE, even for uric acid interference.

In accord with the invention, the silver halide layer of the electrode is treated with a selected inorganic or organic acid, or a salt thereof having certain required properties, in a concentration and for a time effective to reduce the negative bias. The acids that are useful for this purpose have a pKa of less than 4.0, and do not dissolve silver chloride, that is, have a silver solubility product less than 10.0, e.g., nitric acid, sulfuric acid, phosphoric acid, hydrochloric acid, formic acid, lactic acid and the like, as well as mixtures of these. If the pKa is >4.0, then the acid is too weak to have an effect. If the pK_(sp) is >10.0, then it will dissolve silver chloride, which is unacceptable. Of these acids, the most preferred are those having a silver complexation constant K_(c) <100, e.g., nitric acid and phosphoric acid.

It has also been found that certain acid salts are useful as an alternative to the above-noted acids, namely those in which the salt:

(i) is soluble in water at ≧0.001M,

(ii) yields an aqueous pH of ≦7.0, and

(iii) comprises ions that do not dissolve the silver chloride, the cations being univalent or divalent cations only.

Salts that fail to provide these conditions are unsatisfactory; thus not all acid salts can be used. (For example, mercuric salts and salts of Br.sup.⊖ and I.sup.⊖ tend to dissolve the AgCl.) A solution of the following salts is highly preferred: NaNO₃, Ca(NO₃)₂, CdSO₄ or FeSO₄ at a concentration of at least 0.015M, for a length of time of between about 0.5 min and about 5 min.

It has been found that the order in which the silver chloride layer is treated with this acid or salt is not particularly critical. That is, the treatment can occur either immediately after the oxidation step used to convert the surface of the silver layer to silver chloride, e.g., while, it is still wet. Alternatively, the electrode so converted can be dried, aged, and thereafter treated. In any event, the treatment comes before the electrode is overcoated, if at all, with the cellulose ester overcoat described above. It may, of course, be necessary to adjust treatment conditions to ensure that the AgCl layer is not significantly dissolved during the treatment. Furthermore, AgCl layers that have been dried and aged (but not yet overcoated) require and also tolerate a greater acid strength, for a given residence time, to produce the same reduction in purine negative bias as is achieved when the AgCl layer is treated fresh and wet, out of the oxidizing bath.

Thus, as will be readily apparent, the concentration of the acid or salt as well as the time of residence of the electrode within the acid or salt will vary. Selection of the appropriate values depend primarily upon a) the acid or salt selected and b) whether the treatment is to a fresh AgCl surface, or one that is aged. Selection of an appropriate concentration and residence time within these guidelines is well within the skill of the skilled artisan. By way of example, for treatment with nitric acid, using an electrode having a dried and aged silver chloride layer, the concentration of the acid or salt can be between 0.001M and 1.0M, for a residence time of between about 2000 sec and about 30 sec, respectively. Preferably the concentration is between about 0.01M and about 1.0M for a residence time of the electrode that is between about 300 sec and about 30 sec, respectively. Most preferably, the concentration is no less than about 0.05M with a residence time no greater than about 120 sec.

However, the residence time is preferably much shorter than these figures, or the HNO₃ concentration considerably weaker, if the treatment is applied to a wet, freshly formed AgCl layer.

The selection of concentration and residence time will also depend upon the purine interference that is contempated. That is, if the acid or salt concentration is selected to ensure, e.g., a 10% reduction in observed purine bias, the necessary concentration of acid or salt for a given residence time varies somewhat, depending on the identity of the purine and its test concentration, used for the test. For the purpose of the examples hereinafter described, the purine selected was hypoxanthine at 2 mM.

The following is a simplified test to determine whether a particular acid or salt is useful in this invention: The electrode with its metal chloride layer already formed, and aged at least 1 month, is washed with the candidate acid at the selected strength and for the selected time. An identical electrode having metal chloride of the same age is washed with water as a control, for the same time period. The two electrodes are then checked in the following cell: .sup.⊕ Orion F ISE/100 μl of sample/M/MCl.sup.⊖, where M is the metal of the electrode, and the sample liquid comprises 115 mM NaCl, 25 mM NaHCO₃, 10 mM KF in H₂ O, and 2 mM hypoxanthine. (All mM amounts are expressed per liter, as is conventional.) The cell is read between 1 and 20 sec after spotting, the same read time being made on the control electrode. If at least a 10% reduction is found in the negative bias, compared to the control electrode washed only with water, then the acid or salt, its strength, and its wash time are appropriate.

The selection of a variety of acids or salts for the treatment can also require additional steps. For example, if HCl is used, it is preferred that an H₂ O wash step be used thereafter, which may not be needed for the other acids. The reason of course is to remove Cl.sup.⊖ ions from the AgCl surface and thus to avoid an artificially high Cl.sup.⊖ blank being sensed by the reference liquid on the reference side of the differential measurement.

EXAMPLES

The following examples further illustrate the scope of the invention.

In the following examples, except where otherwise stated, the test cell was the following: .sup.⊕ Orion F ISE/100 μl of sample/Ag/AgCl.sup.⊖. The control fluid comprised 115 mM NaCl, 25 mM NaHCO₃, and 10 mM KF in H₂ O. The purine fluid was the control fluid plus 2 mM hypoxanthine (purine) dissolved therein. The difference in potentials ΔmV, wherein

    .sup.ΔmV=V.sub.purine fluid .sup.-V.sub.control fluid

was measured at the time stated, after metering. It will be appreciated, however, that such attempts to make a single point reading in time are only rough estimates of what is essentially a non-equilibrium condition. Therefore, the same read time was used within a given set of experiments.

Because this test cell is of opposite polarity than in the case of the commercial analyzer test, the sign of the ΔmV data in Tables I and II has been reversed to be consistent with the commercial case in Table III (+ΔmV≃-percent Cl.sup.⊖ bias). In both instances, the purine compounds caused a negative bias on chloride ISE's.

EXAMPLES 1-7 Various Acids

In each example, the AgCl layer of the ISE's was prepared using the above-described potassium chlorochromate bleach, and thereafter dried. After some aging, which varied from example to example, the electrode was dipped into a bath of the stated acid for the stated time. (The control in each example was selected to be exactly the same age as the examples against which it was compared, and was washed only in water.) After the treatment time, they were blotted with filter paper and oven-dried at 50° C. for 5 minutes. No cellulose acetate overcoat was applied. The test in the cell described above was then run, after the time indicated to determine whether the acid treatment produced at least a 20% reduction in the positive ΔmV value noted for the control. The results appear in Table I.

                                      TABLE I                                      __________________________________________________________________________                                           % Reduction                                   Acid Composition                                                                        Residence Read Time     Against                                  Example                                                                             of Bath  Time in Bath (sec)                                                                       After Spotting (sec)                                                                     ΔmV                                                                          Control ΔmV                        __________________________________________________________________________     Control                                                                             None     None      5         2.7 --                                       1    0.005  .sub.--M HNO.sub.3                                                               300       5         -3.0                                                                               ≃200                       Control                                                                             None     None      10        8.15*                                                                              --                                       2    0.15  .sub.--M HNO.sub.3                                                                30        10        -6.1                                                                               175                                      3    0.05  .sub.--M H.sub.3 PO.sub.4                                                         30        10        -9.5                                                                               217                                      4    0.15  .sub.--M HCl                                                                       30**     10        1.3  84                                      5    0.15  .sub.--M formic                                                                   30        10        -2.3                                                                               128                                           acid                                                                      Comp.                                                                               H.sub.2 O with no                                                                       30        10        14.3                                                                               No reduction                             Ex. 1                                                                               acid                                                                      Control                                                                             None     None      5         6.5 --                                       6    0.025  .sub.--M H.sub.2 SO.sub.4                                                        300       5         2.2  66                                      Control                                                                             None     None      3         3.5 --                                       7    0.15  .sub.--M lactic                                                                   30        3         -3.1                                                                               ≃200                            acid                                                                      Comp.                                                                               H.sub.2 O only                                                                          30        3         4.1 No reduction                             Ex. 2                                                                          __________________________________________________________________________      *An average of two readings.                                                   **Followed by a 30 sec H.sub.2 O rinse.                                  

EXAMPLES 8-15 Variations in Concentration and Residence Time

Example 1 was repeated, but for these examples, the concentrations and residence times were those listed in Table II.

                                      TABLE II                                     __________________________________________________________________________                                           % Reduction                                   Acid Composition                                                                        Residence Read Time     Against                                  Example                                                                             of Bath  Time in Bath (sec)                                                                       After Spotting (sec)                                                                     ΔmV                                                                          Control ΔmV                        __________________________________________________________________________     Control                                                                             None     None      30        21.8                                                                               --                                       8    0.1  .sub.--M HNO.sub.3                                                                 120       30        12  41                                       9    0.1  .sub.--M HNO.sub.3                                                                 60        30        8   63                                       10   1.0  .sub.--M HNO.sub.3                                                                 30        30        12  41                                       Control                                                                             None     None      30        17.5                                                                               --                                       11   0.01  .sub.--M HNO.sub.3                                                                1800      30        3.0 77                                       Comp.                                                                               0.01  .sub.--M HNO.sub.3                                                                120       30        19.2                                                                               No reduction                             Ex. 3                                                                          Control                                                                             None     None      5         2.7 --                                       12   0.05  .sub.--M HNO.sub.3                                                                300       5         -3.0                                                                               ≃200                       13   0.01  .sub.--M HNO.sub.3                                                                1800      5         -4.6                                                                               270                                      Control                                                                             None     None      3         2.2 --                                       14   0.05  .sub.--M HNO.sub.3                                                                30        3         1.7 23                                       15   0.1  .sub.--M HNO.sub.3                                                                 30        3         0.9 59                                       Comp.                                                                               0.2  .sub.--M HNO.sub.3                                                                 30        3         5.3 No reduction                             Ex. 4                                                                          __________________________________________________________________________

The two Comparative Examples 3 and 4 were unsuccessful because of an improper combination of acid concentration and residence time. In the case of Comparative Example 3, the residence time was insufficient, whereas it was too long for Comparative Example 4. It is believed in the latter case that there was detrimental removal of the AgCl layer and possibly of the Ag layer.

Conversely, the strength of the acid in Example 10 was not too strong, even though greater in absolute value than the strength of the acid in Comparative Example 4. The reason was that the electrode in Example 10 was much older than the one in Comparative Example 4 (greater than 24 months versus less than 3 months, respectively). The greater aging made Example 10 more tolerant of the greater acid strength.

EXAMPLES 16-17 Results When Overcoated with Cellulose Acetate

The procedure of Example 1 was repeated, except as follows:

The acid wash was applied to a freshly prepared AgCl layer while the latter was still wet, using the same process line as for the bleach bath. After the treatment in the acid noted in Table III, an overcoat of cellulose acetate of a thickness of 10-20 μm was prepared as described in the aforesaid U.S. Pat. No. 4,199,411. The testing of the electrodes was done using a human serum pool spiked with 0.455 mM hypoxanthine. The control was the same, but without the hypoxanthine. The measuring cell was the "Ektachem Cl.sup.⊖ "™ test elements prepared using the noted ISE's, read on the "Ektachem 400"™ analyzer manufactured by Eastman Kodak Co., with electrometer readings being taken after 3 minutes. The "Ektachem" reference fluid was used on the reference side of the test. All electrometer readings were converted to Cl.sup.⊖ concentrations via previously measured calibration lines.

                                      TABLE III                                    __________________________________________________________________________                                            % Reduction                                  Acid Composition                                                                        Residence Read Time % [Cl]*                                                                             Against                                 Example                                                                             of Bath  Time in Bath (sec)                                                                       After Spotting (min)                                                                     Bias Control                                 __________________________________________________________________________     Control                                                                             None     None      3         -9.87                                                                               --                                      16   0.015  .sub.--M HNO.sub.3                                                               ≃30                                                                        3         -1.1  ≃85                      17   0.015  .sub.--M H.sub.3 PO.sub.4                                                        ≃30                                                                        3         +1.32                                                                               ≃113                      __________________________________________________________________________      *% [Cl] bias = 100([Cl] purine  [Cl] control fluid)/[Cl] control fluid.        Replicate precision on any given [Cl] prediction is about ± 0.7%.     

EXAMPLES 18-21 Various Salts

The procedure of Example 16 was repeated, except salts of acids were used to prepare the wash solution, instead of acids. The wash time was the same for the control (no acid salts present, just deionized water) and the salt solutions, namely 3 min. The test fluids and the control fluids were the same as for Ex. 16. The tests were run after an aging period of 1 month, while stored at the temperature indicated in Table IV.

The sodium acetate, comparative ex. #5, was selected because it has an aqueous pH above 7.0. It was unsatisfactory, as shown in Table IV:

                                      TABLE IV                                     __________________________________________________________________________           Salt Composition                                                                        Storage Temp                                                                           % [Cl]*                                                                             % Reduction Against                                Example                                                                              of Bath  While Aging                                                                            Bias Control                                            __________________________________________________________________________     Control                                                                              None-water only                                                                         55° F.                                                                          -16.4                                                                               --                                                                    78° F.                                                                      -35.5                                                                               --                                                 18    Ca(NO.sub.3).sub.2                                                                      42° F.                                                                          -1.0 93.9                                                     (0.015  .sub.--M)                                                                           70° F.                                                                      -5.7 83.9                                               19    FeSO.sub.4 (0.015  .sub.--M)                                                            42° F.                                                                          -8.0 51.2                                                                  70° F.                                                                      -11.1                                                                               68.7                                               20    CdSO.sub.4 (0.015  .sub.--M)                                                            42° F.                                                                          -0.3 98.2                                                                  70° F.                                                                      -1.5 95.8                                               21    Ca(NO.sub.3).sub.2                                                                      42° F.                                                                          -3.7 77.4                                                     (0.424  .sub.--M)                                                                           70° F.                                                                      -3.6 89.9                                               Compar.                                                                              Na Acetate                                                                              42° F.                                                                          -25.1                                                                               worse than control                                 Example 5                                                                            (0.015  .sub.--M)                                                                           70° F.                                                                      -60.2                                                                               worse than control                                 __________________________________________________________________________      *As defined in Example 16 and 17, Table III.                             

EXAMPLE 22 NaNO₃ Solution

The procedure of Example 18 was repeated, except the salt solution of the wash was 0.015M NaNO₃. The ISE was stored at 24° C. for two days, and at -13° C. for a short period, prior to testing. The results appear in Table V:

                  TABLE V                                                          ______________________________________                                                                              %                                                              Read Time       Reduction                                                      After     % [Cl]*                                                                              Against                                   Example                                                                               Salt Composition                                                                             Spotting  Bias  Control                                   ______________________________________                                         Control                                                                               None (Water only)                                                                            3 Min     -9.87 --                                        22     NaNO.sub.3    3 Min     -0.57 94.2                                      ______________________________________                                          *As explained in Table III.                                              

The invention has been described in detail with particular reference to preferred embodiments thereof, but it will be understood that variations and modifications can be effected within the spirit and scope of the invention. 

What is claimed is:
 1. In a process for making an ion selective electrode selective for chloride, comprising the steps of(a) forming a layer of silver on a support, and (b) oxidizing a surface portion of the silver layer with a bath comprising a chlorochromate, to form silver chloride; the improvement comprising a further step, after step (b), of washing said electrode in an organic acid, inorganic acid, or aqueous solution of a salt of said organic or inorganic acid, provided that (a) said acid has a pKa <4.0 and a silver solubility product pK_(sp) <10.0, in a concentration and for a length of time effective to reduce negative biases created by purine interferences when using an electrode prepared without said further step; and (b) said salt;(i) is soluble in water at ≧0.001M, (ii) yields an aqueous pH of ≦7.0, and (iii) comprises ions that do not dissolve said silver chloride, the cations being univalent or divalent cations only.
 2. In a process for making an ion selective electrode selective for chloride, comprising the steps of(a) forming a layer of conductive metal on a support, and (b) oxidizing a surface portion of the metal layer with a bath comprising a chlorochromate to form MCl wherein M is the conductive metal, the improvement comprising a further step, after step (b), of washing said MCl layer in HNO₃ or H₃ PO₄ having a concentration of from about 0.01M to about 1.0M, for a length of time of between about 5 min and about 0.5 min. respectively, such concentration and such length of time being effective to reduce negative purine biases created in the absence of the washing step
 3. In a process for making an ion selective electrode selective for chloride, comprising the steps of(a) forming a layer of conductive metal on a support, and (b) oxidizing a surface portion of the metal layer with a bath comprising a chlorochromate to form MCl wherein M is conductive metal, the improvement comprising a further step, after step (b), of washing said MCl layer in a solution of NaNO₃, Ca(NO₃)₂, CdSO₄ or FeSO₄ at a concentration of at least 0.015M, for a length of time of between about 0.5 min and about 5 min.
 4. A process as defined in claim 2 or 3, and further including, after said washing step, the step of forming a layer of cellulose ester on said layer of MCl.
 5. A process as defined in claim 2 or 3, wherein said chlorochromate comprises potassium chlorochromate in a concentration of from about 0.002 to about 0.2M.
 6. A process as defined in claim 2 or 3, and further including, after said washing step, the step of washing the metal chloride layer with water. 